High Alumina Refractory Castable
Cov ntaub ntawv khoom
| Khoom npe | Refractory Castable |
| Pawg | Tsawg Cement Castable / High Strength Castable /High Alumina Castable / Lub teeb yuag Castable |
| Kev sib xyaw | Refractory aggregates, hmoov thiab binders |
| Nta | 1. Kev tsim kho yooj yim, 2. Zoo Slag Resistance, 3.Good Corrosion Resistance, 4.Qhov hluav taws kub zoo, 5.Kev txuag hluav taws xob thiab kev tiv thaiv ib puag ncig. |
| Daim ntawv thov | Dav siv nyob rau hauv ntau yam kub kub Industrial rauv. |
| Cov khoom | Tsawg Cement Castable | Siab zog Castable |
| Kev piav qhia | Tsawg cement castables xa mus rau castables tshiab nrog me ntsis cement binder.Cov ntsiab lus cement ntawm refractory castables feem ntau yog 15% mus rau 20%, thiab cov cement cov ntsiab lus ntawm cov cement castables tsawg yog li 5%, thiab qee qhov txawm txo mus rau 1% mus rau 2%. | Lub zog hnyav hnav-tiv taus castable yog tsim los ntawm lub zog loj sib sau ua ke, ntxhia cov khoom sib xyaw ua ke, siab zog sib sau ua ke thiab tiv thaiv tawg thiab hnav-tiv taus tus neeg sawv cev. |
| Nta | Thermal shock resistance, slag resistance, thiab erosion resistance yog qhov zoo dua, zoo dua li cov cib refractory. | Lub zog muaj zog, siab hnav tsis kam, cuam tshuam tsis kam, yaig tsis kam, tiv thaiv roj permeability, arbitrary zoo tswj, muaj zog ncaj ncees, kev tsim kho yooj yim, kev tsim kho zoo, thiab kev pabcuam ntev. |
| Daim ntawv thov | 1.Lining ntawm ntau yam kev kho cua sov furnaces, cua sov rauv, ncej kilns, teb kilns, hluav taws xob rauv npog, moj tej tawg rauv tapholes; 2.Self-flowing low-cement castables are suited for high-temperature spray guns linings for spray metallurgy and petrochemical catalytic cracking reactors Wear-resistant lining, txheej txheej ntawm cua sov rauv dej-txias yeeb nkab, thiab lwm yam. | Sab hauv hnav-resistant txheej ntawm slag sluice,ore trough, thee spout, hopper thiab silo hauv metallurgy, thee, thermal zog, tshuaj,cement thiab lwm yam kev lag luam, thiab lub tshuab hluav taws xob sib tov sib xyaw silo, sintering silo, feeder, pelletizer, thiab lwm yam. |
| Cov khoom | High Alumina Castable | Lub teeb yuag Castable |
| Kev piav qhia | High-alumina castables yog refractorycastables ua los ntawm high-alumina raw khoomas aggregates thiab hmoov, thiab ntxivnrog binders. | Lub teeb castable nrog tsawg ntom ntom yog ua los ntawm aluminate cement, siab alumina zoo khoom, ceramsite, thiab additives. |
| Nta | Nws muaj lub zog txhua yam thiab zoo thermal poob siab tsis kam, abrasion tsis kam thiab lwm yam khoom. | Kev ceev qis, me thermal rwb thaiv tsev cov txiaj ntsig, kua qaub thiab rwb thaiv tsev cua sov, thiab dej kub. |
| Daim ntawv thov | Nws yog tsuas yog siv nyob rau hauv lub puab txheej ntawm boilers, moj tej tawg rauv kub moj tej tawg qhov cub, cua sov rauv, ceramic kilns thiab lwm yam kilns. | Lub teeb castable yuav siv tau rau cov thermal rwb thaiv tsev txheej ntawm high-temperature industrial furnace thiab cov cuab yeej siv rau hauv ob sab phlu ntawm ntau yam high-temperature gas pipes. |
Product Index
Kub Blast Qhov cub
Tunnel Kiln
Rotary Kiln
Hlau thiab steel kev lag luam: feem ntau yog siv rau kev kho thiab patching ntawm hluav taws xob arc rauv, steelmaking furnaces, ladles thiab lwm yam khoom siv.
Kev lag luam hlau tsis-ferrous: siv rau patching thiab kho cov tooj liab, txhuas, zinc, npib tsib xee thiab lwm yam uas tsis yog-ferrous hlau smelting furnaces thiab converters.
Kev lag luam iav: siv rau kev txij nkawm thiab thaj ua haujlwm ntawm cov iav rauv, annealing furnaces thiab lwm yam khoom siv.
| Khoom npe | Tsawg Cement Castable | |||||
| INDEX | RBTZJ-42 | RBTZJ-60 | RBTZJ-65 | RBTZJS-65 | RBTZJ-70 | |
| Ua hauj lwm txwv kub | 1300 | 1350 | 1400 | 1400 | 1450 | |
| Qhov ceev (g / cm3)110 ℃ × 24h ≥ | 2.15 | 2.3 | 2.4 | 2.4 | 2.45 Nws | |
| Txias khoov zog110 ℃ × 24h (MPa) ≥ | 4 | 5 | 6 | 6 | 7 | |
| Txias Crushing Zog (MPa) ≥ | 110 ℃ × 24 teev | 25 | 30 | 35 | 35 | 40 |
| CT ℃ × 3 h | 50 1300 ℃ × 3 h | 55 1350 ℃ × 3 h | 60 1400 ℃ × 3 h | 40 1400 ℃ × 3 h | 70 1400 ℃ × 3 h | |
| Permanent Linear Hloov@CT ℃ × 3h(%) | -0.5 ~ + 0.5 1300 ℃ | -0.5 ~ + 0.5 1350 ℃ | 0 ~ + 0.8 hli 1400 ℃ | 0 ~ + 0.8 hli 1400 ℃ | 0 ~ + 1.0 1400 ℃ | |
| Thermal Shock Resistance (1000 ℃ dej) ≥ | - | - | - | 20 | - | |
| Al2O3 (%) ≥ | 42 | 60 | 65 | 65 | 70 | |
| CaO(%) ≤ | 2-3 | 2-3 | 2-3 | 2-3 | 2-3 | |
| Fe2O3(%) ≤ | 2.0 | 1.5 | 1.5 | 1.5 | 1.5 | |
| Khoom npe | Siab zog Castable | |||||
| INDEX | TSI-50 | TSI-60 | TSI-70 | TSI-80 | TSI-90 | |
| Ua haujlwm txwv kub (℃) | 1400 | 1500 | 1600 | 1700 | 1800 | |
| 110 ℃ Qhov ntom ntom (g / cm3) ≥ | 2.15 | 2.30 Nws | 2.40 Nws | 2.50 Nws | 2.90 ib | |
| Modulus ntawm Repture (MPa) ≥ | 110 ℃ × 24 teev | 6 | 8 | 8 | 8.5 | 10 |
| 1100 ℃ × 3 h | 8 | 8.5 | 8.5 | 9 | 9.5 ib | |
| 1400 ℃ × 3 h | 8.5 1300 ℃ × 3 h | 9 | 9.5 ib | 10 | 15 | |
| Txias Crushing Zog (MPa) ≥ | 110 ℃ × 24 teev | 35 | 40 | 40 | 45 | 60 |
| 1100 ℃ × 3 h | 40 | 50 | 45 | 50 | 70 | |
| 1400 ℃ × 3 h | 45 1300 ℃ × 3 h | 55 | 50 | 55 | 100 | |
| Permanent Linear Change(%) | 1100 ℃ × 3 h | -0.2 | -0.2 | -0.25 | -0.15 | -0.1 |
| 1400 ℃ × 3 h | -0.45 1300 ℃ × 3 h | -0.4 | -0.3 | -0.3 | -0.1 | |
| Al2O3 (%) ≥ | 48 | 48 | 55 | 65 | 75 | 90 |
| CaO(%) ≤ | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 | 4.0 |
| Fe2O3(%) ≤ | 3.5 | 3.5 | 3.0 | 2.5 | 2.0 | 2.0 |
| Khoom npe | High Alumina Castable | ||||||
| INDEX | Al2O3 (%) ≥ | CaO(%) ≥ | Refractoriness (℃) | CT ℃ × 3h PLC ≤1% | 110 ℃ Tom qab ziab (MPa) | ||
| CCS | MOR | ||||||
| Clay Bonded | NL-45 | 45 | - | 1700 | 1350 | 8 | 1 |
| NL-60 | 60 | - | 1720 | 1400 | 9 | 1.5 | |
| NL-70 | 70 | - | 1760 | 1450 | 10 | 2 | |
| Cement Bonded | Qauv: GL-42 | 42 | - | 1640 | 1350 | 25 | 3.5 |
| GL-50 | 50 | - | 1660 | 1400 | 30 | 4 | |
| ZPO-60 | 60 | - | 1700 | 1400 | 30 | 4 | |
| Qauv: GL-70 | 70 | - | 1720 | 1450 | 35 | 5 | |
| Qauv: GL-85 | 85 | - | 1780 | 1500 | 35 | 5 | |
| Tsawg Cement Bonded | DL-60 | 60 | 2.5 | 1740 ib | 1500 | 30 | 5 |
| TXL-80 | 80 | 2.5 | 1780 | 1500 | 40 | 6 | |
| Phosphate Bonded | TXL-45 | 45 | - | 1700 | 1350 | 20 | 3.5 |
| TXL-60 | 60 | - | 1740 ib | 1450 | 25 | 4 | |
| LWM-75 | 75 | - | 1780 | 1500 | 30 | 5 | |
| Sodium Silicate Bonded | IB-40 | 40 | - | - | 1000 | 20 | - |
| Khoom npe | Lub teeb yuag Castable | ||||||
| Ua hauj lwm txwv kub | 1100 | 1200 | 1400 | 1500 | 1600 | ||
| 110 ℃ Qhov ntom ntom (g / cm3) ≥ | 1.15 | 1.25 | 1.35 Nws | 1.40 Nws | 1.50 ib | ||
| Modulus ntawm Repture (MPa) ≥ | 110 ℃ × 24 teev | 2.5 | 3 | 3.3 | 3.5 | 3.0 | |
| 1100 ℃ × 3 h | 2 | 2 | 2.5 | 3.5 | 3.0 | ||
| 1400 ℃ × 3 h | - | - | 3 | 10.8 | 8.1 | ||
| Txias Crushing Strength (MPa) ≥ | 110 ℃ × 24 teev | 8 | 8 | 11 | 12 | 10 | |
| 1100 ℃ × 3 h | 4 | 4 | 5 | 11 | 10 | ||
| 1400 ℃ × 3 h | - | - | 15 | 22 | 14 | ||
| Permanent Linear Change(%) | 1100 ℃ × 3 h | -0.65 1000 ℃ × 3 h | -0.8 | -0.25 | -0.15 | -0.1 | |
| 1400 ℃ × 3 h | - | - | -0.8 | -0.55 Nws | -0.45 Nws | ||
| Thermal conductivity (W/mk) | 350 ℃ | 0.18 | 0.20 ib | 0.30 Nws | 0.48 ib | 0.52 ib | |
| 700 ℃ | 0.25 | 0.25 | 0.45 ib | 0.61 ib | 0.64 ib | ||
| Al2O3 (%) ≥ | 33 | 35 | 45 | 55 | 65 | ||
| Fe2O3(%) ≤ | 3.5 | 3.0 | 2.5 | 2.0 | 2.0 | ||